Scope of Application:
Designed for iron-, nickel-, cobalt-, aluminum-, and copper-based alloys suited to vacuum induction melting and gas atomization. The resulting powders can be used in additive manufacturing, laser cladding, thermal spraying, powder metallurgy, and hot isostatic pressing.
| Name: | Electrode Induction Gas Atomization System |
| Electrode Diameter: | 30-100 mm |
| Electrode Length: |
200-1,000 mm; custom specifications available |
| Maximum Melting Temperature: | 2,200°C |
| Melting Power: | 60-120 kW |
| Ultimate Vacuum: |
6.67 × 10⁻¹ Pa (empty chamber, cold condition) |
| Pressure Rise Rate: |
≤2 Pa/h |
| Production Capacity: | 15-30 kg/h |
| Atomization Gas Pressure: | 0-6 MPa; nozzle pressure rating: 8 MPa |
| Atomization Gas Pressure: | 10-35 Nm³/min |
| Typical Powder Size Fractions: | 15-53 µm, 53-150 µm, 75-200 µm, and 100-250 µm |
| System Dimensions: | Determined by system configuration and project conditions |
Note: Parameters may be adjusted for project requirements and are subject to the final technical agreement.